Composition Chlorinated rubber as the base material, cuprous oxide and a variety of organic antifouling agents and other non-organic tin antifouling agent of the discoloration wooden boat antifouling paint.

Key Features

              · Can effectively prevent the decay of wood and ship maggots, food wood insects on wood decay

              · It can prevent the fouling of marine fouling organisms

              · Can increase the rate of fishing vessels, reduce the cost of repair and extend the life of wooden boats

              · After the film contact with the sea water gradually turn from red to gray green close to the color of the sea, not scared scattered fish

              * Fast drying, good adhesion, resistance to seawater shock

              · It has been approved by the Ministry of Agriculture

Uses Applicable to the wooden bottom of the ship in order to prevent marine adhesion organisms, marine maggots and food wood insects on wood decay and defacement of the bottom.

The appearance of iron red, contact with water into gray-green.

Construction parameters

               Volume of solid 55 ± 3% (according to GB / T9272 eqv ISO3233: 1998 provisions of the determination)

               The dry film thickness is 40mm

               Wet film thickness 73mm

               The theoretical amount of 121g / m2

               A flash point of 25 ° C

               Drying time

 復涂間隔時間

Recommended coating Road 2, dry film thickness greater than 80mm is appropriate.

Before the road matching paint can be directly painted in the tassel lime linen filled wooden boat bottom, can also be used 616 chlorinated rubber iron red thick slurry antirust paint, and then painted 814 wood antifouling paint.

Surface treatment

              · The bottom timber must be dry before painting

              · The new ship should be filled with putty and linen cracks and holes, to be dry after painting wood antifouling paint two

              · If the bottom of an old ship has been attached to marine life, the majority of the paint has been damaged, you must remove the marine organisms and the removal of the old paint film, washed with fresh water, filling putties and holes, After drying paint wood antifouling paint

              · The bottom of the ship is too late to dry, can be used to speed up the drying roast method

Construction conditions

              • Substrate temperature should be above 3 ℃ above dew point

              · Relative humidity not more than 85%

Coating method

  Air spraying

              Diluent 101 Diluent

              Dilution 0-5% (by weight of paint)

              Nozzle diameter of 2.0-3.0mm

              Air pressure 0.3-0.5MPa (about 3-5kg / cm2)

 Brush / roller

              Diluent 101 Diluent

              Dilution 0-3% (by weight of paint)

detergent 

101 diluent

Safety measures refer to Anhui New Material Co., Ltd. Product Safety Data Sheet (MSDS).

Packaging 20L barrels 28kg

                  10L barrels 15kg

Shelf life of 12 months

Additional information on the interval between antifouling paint launches

Remark For the correct use of our products, please carefully read the "User's Guide" in this manual.

Statement The above data and data are based on our test and practical experience in the use of accumulated and can be used as construction guide. We do not understand the situation in the construction, we only guarantee the quality of the paint itself, other issues will not be responsible. For this manual, we will be based on the continuous improvement of products have the right to modify.