          706 anti-rust paint

          Product introduction

          Form :
          Main characteristics :
          Purpose :
          Appearance :

          Composed of synthetic resin-based materials, zinc phosphate, red iron oxide, aluminum powder and other anti-rust pigments, fillers, additives and solvents and other components.

          Key Features

                         Zinc phosphate as the main anti-rust paint, lead-free, non-toxic

                          Has good anti-rust performance

                         * Dry faster

          Use Apply to the ship above the waterline and onshore steel structure for antirust paint surface, with phenolic, alkyd and other traditional type of finish matching.

          The appearance of red and gray

          Construction parameters

                         Volume of solid 49 3% (according to GB / T9272 eqv ISO3233: 1998 provisions of the determination)

                         The dry film thickness is 40mm

                         Wet film thickness 82mm

                         Theoretical amount of 102g / m2

                         A flash point of 35 C

                         Drying time (25 )

                         Table dry 3h

                         Hard work 24h

          Overcoating interval time

          The shortestlongest

          Recommended coating number 2, dry film thickness 80mm

          After the Road supporting the use of various types of alkyd or phenolic type of intermediate paint or finish

          Surface treatment

                        Scaled steel: sandblasted to Sa2 grade; acid pickling method can be used to remove oxide and rust

                        * No oxide steel: to the elastic grinding wheel to St3 level, or sandblasting treatment to Sa2 level

                        Steel coated with shop primer: paint film damage and corrosion at the second rust, polished to St3 level

                        * Welding, flame cutting or fire correction Combustion: polished to St3 level

          Construction conditions

                        • Substrate temperature should be above 3 above dew point

                        Relative humidity not more than 85%

          Coating method

          Airless spray

                    Diluent 104 Diluent

                    Dilution 0-5% (by weight of paint)

                    Nozzle diameter 0.4-0.5mm

                    The discharge pressure was 12 to 15 MPa (about 120 150 kg / cm2)

          Air spraying

                        Diluent 104 Diluent

                        Dilution 0-10% (by weight of paint)

                        Nozzle diameter of 2.0-3.0mm

                        Air pressure 0.3-0.4MPa (about 3-4kg / cm2)

          Roll coating / brushing

                    Diluent 104 Diluent

                    Dilution 0-3% (by weight of paint)

          Cleaner 104 Diluent

          Safety measures refer to Tianchang Kailin Chemical Co., Ltd. Product Safety Data Sheet (MSDS).

          Packaging 20L drums 24kg

          Shelf life of 12 months

          Remark For the correct use of our products, please carefully read the "User's Guide" in this manual.

          Statement The above data and data are based on our test and practical experience in the use of accumulated and can be used as construction guide. We do not understand the situation in the construction, we only guarantee the quality of the paint itself, other issues will not be responsible. For this manual, we will be based on the continuous improvement of products have the right to modify.

          If you have questions, you can

          Or leave a message for us.

          Related recommendation
          Online Service




              <address id="9hx9l"></address>
              <form id="9hx9l"></form>
                <form id="9hx9l"></form>

                <form id="9hx9l"></form>