Composed of chlorinated rubber, plasticizers, aluminum powder and other anti-rust paint, additives and solvents composed of anti-rust paint.

Key Features

               Water vapor and oxygen permeability of the paint film is low, with excellent water resistance and good corrosion resistance

               Dry fast, several times faster than the oil-based paint dry

               · Excellent low-temperature construction performance, can be -20 ℃ ~ 50 ℃ environment construction

               · Film has good adhesion to steel

               · The coating layer is miscible with the layer and has excellent interlayer adhesion. In the old paint on the chlorinated rubber re-maintenance coating, do not have to get rid of a solid old paint, easy maintenance

               In the seawater film does not saponification, and cathodic protection have a good supporting sex

               · Has good durability

               · Type approval by China Classification Society

Uses Applicable to anti-corrosion of ship bottom, marine waterline, offshore steel structure and other steel structure.

Appearance 615-1 silvery white, 615-2 light aluminum red

Construction parameters

* pressGB/T9272 eqv ISO3233:1998Specified determination）
Drying time

Overcoating interval time

Recommended coating Road 2, dry film thickness greater than 120mm

702 epoxy zinc-rich shop primer or 703 epoxy iron red shop primer, 704 inorganic zinc silicate shop primer, or direct painting in line with the quality requirements of steel derusting surface.

After the road supporting the paint 616 chlorinated rubber iron red thick slurry antirust paint, or colored chlorinated rubber topcoat.

Surface treatment

               * There are oxide steel: sandblasting to Sa2.5 level

               · No oxide steel: Elastic grinding wheel grinding to St3 or sandblasting to Sa2.5

               · Steel coated with shop primer: secondary rust of paint film damage and corrosion, sanding with elastic grinding wheel to St3 level

               * Welding, flame cutting or fire correction burned parts: the elastic grinding wheel grinding to St3 level

Construction conditions

               • Substrate temperature should be above 3 ℃ above dew point

               · Relative humidity not more than 85%

Coating method

Airless spray

          Diluent 101 Diluent

          Dilution 0-5% (by weight of paint)

          Nozzle diameter 0.4-0.5mm

          The discharge pressure is 15 to 20 MPa (about 150 to 200 kg / cm2)

Air spraying

              Diluent 101 Diluent

              Dilution 0-10% (by weight of paint)

              Nozzle diameter of 2.0-3.0mm

              Air pressure 0.3-0.4MPa (about 3-4kg / cm2)

Roll coating / brushing

              A coating can not achieve the recommended dry film thickness

              Diluent 101 Diluent

              Dilution 0-3% (by weight of paint)

Cleaner 101 Diluent

For safety measures, please refer to the Material Safety Data Sheet (MSDS) of Anhui Kailin New Material Co., Ltd. (formerly Tianchang Kailin Chemical Co., Ltd.).

Packaging 20L drums 24kg

Shelf life of 12 months

Remark For the correct use of our products, please carefully read the "User's Guide" in this manual.

Statement The above data and data are based on our test and practical experience in the use of accumulated and can be used as construction guide. We do not understand the situation in the construction, we only guarantee the quality of the paint itself, other issues will not be responsible. For this manual, we will be based on the continuous improvement of products have the right to modify.