Composed of chlorinated rubber, excellent performance of anti-rust paint, plasticizers, additives and solvents such as the composition of the anti-rust paint.
Key Features
Water vapor and oxygen permeability of the paint film is low, with good water resistance and good corrosion resistance
Dry fast, dry several times faster than oil-based paint
· Excellent low-temperature construction performance, can be -20 ℃ ~ 50 ℃ environment construction
· Film has good adhesion to steel
· The coating layer is miscible with the layer and has excellent interlayer adhesion. In the old paint on the chlorinated rubber re-maintenance of the coating, do not have to get rid of a solid old film, easy maintenance
· Has good durability
Uses
Applicable to ship above the waterline parts, in-cabin, and a variety of onshore steel structure for rust-proof primer surface, but should not be used for flooding parts.
Appearance 625-1 light gray, 625-2 pink
Construction parameters
| product code | 625-1 | 625-2 |
| Volume solids % * | 43±3 | 44±3 |
| Dry film thickness mm | 60 | 60 |
| Wet film thickness mm | 140 | 136 |
| Theoretical consumption g／m2 | 189 | 184 |
| Flash point ℃ | 31 | 31 |
*（According to GB / T9272 eqv ISO3233: 1998 provisions of the determination）
Drying time
| temperature | 5℃ | 20℃ | 30℃ |
| Table dry | 4h | 2h | 1h |
| Hard work | 24h | 12h | 8h |
Overcoating interval time
| temperature | 5℃ | 20℃ | 30℃ |
| The shortest | 12h | 8h | 6h |
| longest | Unlimited | ||
Recommended coating Road 2-3 Road, dry film thickness 120-180mm
702 epoxy zinc-rich shop primer or 703 epoxy iron red shop primer, 704 inorganic zinc silicate shop primer, or direct painting in line with the quality requirements of steel derusting surface.
After supporting the use of paint chlorinated rubber anti-rust paint and colored chlorinated rubber finish.
Surface treatment
* There are oxide steel: sandblasting to Sa2.5 level
· No oxide steel: Elastic grinding wheel grinding to St3 level, or sandblasting to Sa2.5
· Steel coated with shop primer: secondary rust of paint film damage and corrosion, sanding with elastic grinding wheel to St3 level
* Welding, flame cutting or fire correction burned parts: the elastic grinding wheel grinding to St3 level
Construction conditions
• Substrate temperature should be above 3 ℃ above dew point
· Relative humidity not more than 85%
Coating method
Airless spray
Diluent 101 Diluent
Dilution 0-5% (by weight of paint)
Nozzle diameter 0.4-0.5mm
The discharge pressure is 15 to 20 MPa (about 150 to 200 kg / cm2)
Air spraying
Diluent 101 Diluent
Dilution 0-10% (by weight of paint)
Nozzle diameter of 2.0-3.0mm
Air pressure 0.3-0.4MPa (about 3-4kg / cm2)
Roll coating / brushing
A coating can not achieve the recommended dry film thickness
Diluent 101 Diluent
Dilution 0-3% (by weight of paint)
Cleaner 101 Diluent
For safety measures, please refer to the Material Safety Data Sheet (MSDS) of Anhui Kailin New Material Co., Ltd. (formerly Tianchang Kailin Chemical Co., Ltd.).
Packaging 20L drums 24kg
Shelf life of 12 months
Remark For the correct use of our products, please carefully read the "User's Guide" in this manual.
Statement The above data and data are based on our test and practical experience in the use of accumulated and can be used as construction guide. We do not understand the situation in the construction, we only guarantee the quality of the paint itself, other issues will not be responsible. For this manual, we will be based on the continuous improvement of products have the right to modify.