Composition of iron oxide red, epoxy resin and polyamide curing agent made of two-component epoxy red iron shop primer.

Key Features

             · Good anti-rust performance, the film thickness of 25μm, the maintenance period of 3-6 months

             · Film does not contain zinc, welding cutting does not produce harmful gases

             * Fast dry, only a very short period of time that can transport, stacking and painting after painting

             · Excellent welding and cutting performance, the film thickness within the specified range, does not affect the welding cutting performance

             · Excellent adhesion and impact resistance

             · Good oil resistance, water resistance and solvent resistance

             · Compatible with most paint systems

             · Type approval by China Classification Society

Uses Used in workshops, heavy machinery plants, steel plants and other pretreatment lines for shop primer, the maintenance period of about 3-6 months

The appearance of iron red, no light

Construction parameters

              Volume of solid 28 ± 3% (according to GB / T9272 eqv ISO3233: 1998 requirements) (after mixing)

              Component A: Component B = 5: 2 (weight ratio)

              Dry film thickness of 25μm

              The wet film thickness was 89 μm

              Theoretical amount of 102g / m2

              Flash point A (base material) 5 ℃

                             Component B (curing agent) 5 ℃

              Curing time (after mixing) (25 ℃) 30min

              Drying time (25 ℃)

                      Table dry ≤ 5min

                      Hard work ≤ 24h

                      Fully cured 7d

                      Pipeline drying time (preheated steel 50 ℃, bake temperature 120 ℃) ≤ 5min

 Painting interval.

 Can use the time (A, B mixed)

It is recommended that the number of coating channels 1, dry film thickness 25μm.

After supporting paint with chlorinated rubber, epoxy, epoxy asphalt, asphalt, epoxy ester, phenolic, alkyd and other systems supporting the use of paint

Surface treatment Steel sandblasting to Sa2.5, surface roughness 30-75μm

Construction conditions · Substrate temperature should be above 3 ℃ above dew point

                      · When the temperature is lower than 5 ℃, curing reaction of epoxy and curing agent is stopped, and it is not suitable for outdoor construction

                      · Relative humidity not more than 85%

Coating method

Airless spray

          Thinner 106 Thinner

          Dilution 0-10% (by weight of paint)

          Nozzle diameter 0.4-0.5mm

          The discharge pressure was 15 MPa (about 150 kg / cm2)

Air spraying

          Thinner 106 Thinner

          Dilution 0-10% (by weight of paint)

          The nozzle diameter is 2.0-2.5mm

          Air pressure 0.3-0.6MPa (3-6kg / cm2)

Roll coating / brushing

              Only small area repair

              Thinner 106 Thinner

              Dilution 0-3% (by weight of paint)

detergent 

103 diluent

Safety measures

See Anhui Kai Lin New Material Co., Ltd. (formerly Tianchang Kailin Chemical Co., Ltd.) Product Safety Data Sheet (referred to as MSDS).

Packaging Ingredients (Base) 20 L Bottled 16 kg

                  Component B (curing agent) 10 L in drum 6.4 kg

Shelf life of 12 months

Remark For the correct use of our products, please carefully read the "User's Guide" in this manual.

Statement The above data and data are based on our test and practical experience in the use of accumulated and can be used as construction guide. We do not understand the situation in the construction, we only guarantee the quality of the paint itself, other issues will not be responsible. For this manual, we will be based on the continuous improvement of products have the right to modify.