Composition of the epoxy resin, polyamide curing agent, red iron oxide, zinc yellow, additives and solvents composed of two-component epoxy antirust paint.

Key Features

              · Film has good anti-rust and durability

              · Excellent adhesion and impact resistance

              · Good oil resistance and solvent resistance

              · Has good water resistance, salt water resistance and salt spray performance

              With epoxy type, polyurethane type finish has good matching and has good interlayer adhesion

Use Applicable to steel structure, shipbuilding, heavy machinery, electrical machinery, chemical industry, mining machinery, hydraulic steel structure for the use of anti-rust primer.

The appearance of iron red, no light

Construction parameters

              Volume of solid 51 ± 3% (according to GB / T9272 eqv ISO3233: 1998 requirements) (after mixing)

              Component A: Component B = 26: 3 (weight ratio)

              Dry film thickness 50mm

              Wet film thickness 98mm

              The theoretical amount of 133g / m2

              A flash point of 27 ° C

                            Group B 27 ℃

              Drying time (25 ℃)

                         Table dry ≤ 2h

                         Hard work ≤ 24h

                         Fully cured 7d

Curing time (after mixing) (20 ° C) 30 min

Available time (after mixing)

Overcoating interval time

It is recommended to spray the coating with no air or spray 1-2 Road, brush, roller 2-3 Road, dry film thickness greater than 100mm.

After the Road supporting paint 842 epoxy cloud iron antirust paint, or epoxy-type finish, polyurethane topcoat.

Surface treatment

              * There are oxide steel: sandblasting to Sa2.5 level

              * No oxide steel: sandblasting to Sa2.5 level or to the abrasive wheel grinding to St3 level

              • Steel coated with shop primer: sandblasted or sanded with a flexible grinding wheel to St3 level

              · Welding, flame cutting or firework correction Burning parts: remove welding slag, splash, polished smooth, with elastic grinding wheel to St3 level

Construction conditions

              • Substrate temperature should be above 3 ℃ above dew point

              · When the temperature is lower than 5 ℃, curing reaction of epoxy and curing agent is stopped, so it is not suitable for outdoor construction

              · Relative humidity not more than 85%

Coating method

Airless spray

          Diluent 103 Diluent

          Dilution 0-5% (by weight of paint)

          Nozzle diameter 0.4-0.5mm

          The discharge pressure is 20 to 25 MPa (about 200 to 250 kg / cm2)

Air spraying

          Not recommended for large areas of construction, only for small areas of repair or small to be painted parts

          Diluent 103 Diluent

          Dilution 0-10% (by weight of paint)

          Nozzle diameter of 2.0-3.0mm

          Air pressure 0.3-0.4MPa (about 3-4kg / cm2)

Roll coating / brushing

              Diluent 103 Diluent

              Dilution 0-3% (by weight of paint)

Cleaning agent 103 Thinner

Safety precautions Refer to the MSDS.

Packaging a group of 20L barrels 26kg

                  Group B is packed in 3L in 4L

Shelf life of 12 months

Remark For the correct use of our products, please carefully read the "User's Guide" in this manual.

Statement The above data and data are based on our test and practical experience in the use of accumulated and can be used as construction guide. We do not understand the situation in the construction, we only guarantee the quality of the paint itself, other issues will not be responsible. For this manual, we will be based on the continuous improvement of products have the right to modify.