          H53-33 epoxy aluminum tripolyphosphate antirust paint

          Product introduction

          Form :
          Main characteristics :
          Purpose :
          Appearance :

          Composed of epoxy resin, polyamide curing agent, aluminum tripolyphosphate, red iron oxide, such as pollution-free anti-rust paint, additives and solvents composed of two-component epoxy anti-rust paint.

          Key Features

          The use of pollution-free anti-rust paint is conducive to environmental protection

          Film has excellent water resistance and seawater resistance and salt spray resistance.

          Tough film has excellent adhesion and impact resistance.

          * Film has good oil resistance and solvent resistance.

          With epoxy, polyurethane and other topcoats have a good supporting performance.

          Film has good anti-rust performance and durability.

          Uses Applicable to steel structures such as ports, docks, heavy machinery, mining machinery, electric power machinery, water conservancy projects, and steel structures above the waterline of ships.

          Appearance iron red, gray

          Construction parameters

                        Volume of solid 54 3% (according to GB / T9272 eqv ISO3233: 1998 requirements) (after mixing)

                        Part A: Part B = 26: 3 (weight ratio)

                        Dry film thickness 50mm

                        Wet film thickness 93mm

                        Theoretical amount of 140g / m2

                        A flash point of 27

                                       Group B 27

                        Drying time (25 )

                                    Table dry 2h

                                    Hard work 24h

                                    Fully cured 7d

          Curing time (after mixing) (20 C) 30 min

          Available time (after mixing)

          The temperature

            5

            20

            30

          40

          Available time 

          12h

          8h

          6h

          4h

          Overcoating interval time

          temperature

            5

            20

            30

          40

          The shortest 

          48h

          24h

          16h

          8h

          longest 

          14d

          7d

          5d

          5d

          It is recommended that the number of coating airless spray 1-2 Road or brush, roller 2, dry film thickness greater than 80mm.

          Before the road supporting paint H06-4 epoxy zinc-rich anti-rust paint, E06-1 inorganic zinc silicate antirust paint, or direct painting in the derusting quality to Sa2.5 level steel surface.

          After the road supporting paint to 842 epoxy cloud iron antirust paint for the middle layer paint, or epoxy type finish, polyurethane topcoat.

          Surface treatment

                        * There are oxide steel: sandblasting to Sa2.5 level

                        * No oxide steel: sandblasting to Sa2.5 level or to the abrasive wheel grinding to St3 level

                        • Steel coated with shop primer: sandblasted or sanded with a flexible grinding wheel to St3 level

                        Welding, flame cutting or firework correction Burning parts: remove welding slag, splash, polished smooth, with elastic grinding wheel to St3 level

          Construction conditions

                        • Substrate temperature should be above 3 above dew point

                        When the temperature is lower than 5 , curing reaction of epoxy and curing agent is stopped, so it is not suitable for outdoor construction

                        Relative humidity not more than 85%

          Coating method

          Airless spray

                    Diluent 103 Diluent

                    Dilution 0-5% (by weight of paint)

                    Nozzle diameter 0.4-0.5mm

                    The discharge pressure is 20 to 25 MPa (about 200 to 250 kg / cm2)

          Air spraying

                    Diluent 103 Diluent

                    Dilution 0-10% (by weight of paint)

                    Nozzle diameter of 2.0-3.0mm

                    Air pressure 0.3-0.4MPa (about 3-4kg / cm2)

          Roll coating / brushing

                        Diluent 103 Diluent

                        Dilution 0-3% (by weight of paint)

          Cleaning agent 103 Thinner

          Safety precautions Refer to the MSDS.

          Packaging a group of 20L barrels 26kg

                           Group B is packed in 3L in 4L

          Shelf life of 12 months

          Remark For the correct use of our products, please carefully read the "User's Guide" in this manual.

          Statement The above data and data are based on our test and practical experience in the use of accumulated and can be used as construction guide. We do not understand the situation in the construction, we only guarantee the quality of the paint itself, other issues will not be responsible. For this manual, we will be based on the continuous improvement of products have the right to modify.


          If you have questions, you can

          Or leave a message for us.

          Related recommendation