Composed of epoxy resin, coal tar pitch, epoxy curing agent, anti-rust pigments, physical pigments, additives and solvents composed of two-component oil tank paint.

Key Features

· Excellent seawater resistance and durability

· Excellent anti-rust performance

· Good oil resistance and chemical resistance

* Has good adhesion, impact resistance, wear resistance

· Airless spray, dry film thickness of up to 125μm

· Type approval by China Classification Society

Use as marine fuel tanks, crude oil tanks, ballast tanks and host base protection coating purposes.

Appearance of silver

Construction parameters

               Volume solids 67 ± 3% (measured according to ISO / IEC 3233: 1998) (after mixing)

               Component A: Component B = 7: 4 (weight ratio)

               The dry film thickness was 125 μm

               The wet film thickness was 187 μm

               Theoretical amount of 220g / m2

               Flash point A component 22 ℃

                              B component of 21 ℃

Drying time

Curing time (20 ° C after mixing) 30 min

Pot life (20 ℃ after mixing) 8h

(When the temperature is higher than 30 ℃, the pot life of Group A and B will be shortened with the temperature increasing.

Overcoating interval time

It is recommended to spray the coating a few Road no air, a brush or roller to be painted 2-3 Road, dry film thickness of 125μm.

702 epoxy zinc-rich shop primer, 703 epoxy zinc oxide shop primer, 704 inorganic zinc silicate shop primer, 842 epoxy cloud iron antirust paint, or direct painting in the derusting quality to achieve Sa2.5 level of the steel plate.

After the Road supporting paint H54-31 (835) black epoxy asphalt paint

Surface treatment

              * There are oxide steel: sandblasting to Sa2.5 level

              · No oxide steel: sandblasted to Sa2.5 level, or to the abrasive wheel grinding to St3 level

              · Coated with workshop primer steel: the use of light sand blasting or elastic grinding wheel in the rust to polish to St3 level

             · Welding, flame cutting or fire work correction Burned parts: remove welding slag, splash, polished smooth, with elastic grinding wheel to St3 level

Construction conditions

             • Substrate temperature should be above 3 ℃ above dew point

             · When the temperature is lower than 5 ℃, epoxy reaction with the curing agent stopped, not suitable for outdoor construction

             · Relative humidity not more than 85%

Coating method

Airless spray

          Diluent 103 Diluent

          Dilution 0-5% (by weight of paint)

          Nozzle diameter 0.4-0.5mm

          The discharge pressure is 20 to 30 MPa (about 200 to 300 kg / cm2)

Air spraying

          Large-area construction is not recommended, only for small-sized repair or small coated parts

          Diluent 103 Diluent

          Dilution 0-10% (by weight of paint)

          Nozzle diameter of 2.0-3.0mm

          Air pressure 0.2-0.4MPa (about 2-4kg / cm2)

Roll coating / brushing

          Mainly used for small area painting and repair

          Diluent 103 Diluent

          Dilution 0-3% (by weight of paint)

Cleaning agent 103 Thinner

Safety precautions Refer to the MSDS.

Packaging A component 20L barrels 14kg

                 Group B 10L barrels 8kg

Shelf life of 12 months

Remark For the correct use of our products, please carefully read the "User's Guide" in this manual.

Statement The above data and data are based on our test and practical experience in the use of accumulated and can be used as construction guide. We do not understand the situation in the construction, we only guarantee the quality of the paint itself, other issues will not be responsible. For this manual, we will be based on the continuous improvement of products have the right to modify.