          746 Iron red epoxy ester primer

          Product introduction

          Form :
          Main characteristics :
          Purpose :
          Appearance :


          Epoxy resin and dry oil fatty acid by esterification reaction epoxy resin as the base material, iron oxide red, physical pigments, additives, desiccant and solvent composed of one-component from the dry-type rust-proof end paint.

          Key Features

                         * Has good anti-rust performance

                          Tough film has good adhesion, impact resistance and flexibility

                         * Antirust performance is better than alkyd, phenolic-type anti-rust paint, but two-component curing type anti-rust paint is poor

          It can be used as the traditional rust-proof primer for onshore steel structure and equipment.

          Appearance iron red

          Construction parameters

                         Volume of solid 42 3% (according to GB / T9272 eqv ISO3233: 1998 provisions of the determination)

                         The dry film thickness was 40 m

                         Wet film thickness of 95m

                         Theoretical amount of 129g / m2

                         A flash point of 27 C

                         Drying time (25 )

                         Table dry 1h

                         Hard work 24h

                         Drying (120 2 ) 1h

          Overcoating interval time





          The shortest






          Recommended coating number 2, dry film thickness 80m.

          After supporting all kinds of paint with alkyd paint, amino baking.

          Surface treatment

                        * There are oxide steel: sandblasting treatment to Sa2 level (acid method can also be used to remove oxide and rust)

                        * No oxide steel: Elastic grinding wheel grinding to St3 level

                        Steel coated with shop primer: paint film damage and corrosion at the second rust, polished to St3 level

                        * Welding, flame cutting or fire correction Combustion: polished to St3 level

          Construction conditions

                        • Substrate temperature should be above 3 above dew point

                        Relative humidity not more than 85%

          Coating method

          Airless spray

                    Diluent 103 Diluent

                    Dilution 0-5% (by weight of paint)

                    Nozzle diameter 0.4-0.5mm

                    The discharge pressure is 12 to 15 MPa (about 120 to 150 kg / cm2)

           Air spraying

                        Diluent 103 Diluent

                        Dilution 0-5% (by weight of paint)

                        Nozzle diameter of 2.0-3.0mm

                        Air pressure 0.3-0.4MPa (about 3-4kg / cm2)

          Roll coating / brushing

                   Diluent 103 Diluent

                   Dilution 0-3% (by weight of paint)

          Cleaning agent 103 Thinner

          Safety precautions Refer to the MSDS.

          Packaging 20L barrels 28kg

          Shelf life of 12 months

          Remark For the correct use of our products, please carefully read the "User's Guide" in this manual.

          Statement The above data and data are based on our test and practical experience in the use of accumulated and can be used as construction guide. We do not understand the situation in the construction, we only guarantee the quality of the paint itself, other issues will not be responsible. For this manual, we will be based on the continuous improvement of products have the right to modify.

          If you have questions, you can

          Or leave a message for us.