          14 Silicone high temperature baking varnish

          Product introduction

          Form :
          Main characteristics :
          Purpose :
          Appearance :

          Composed of silicone resin, aluminum powder and organic solvents and other components of the high temperature paint.

          Key Features

                        · Good heat resistance, can be used in the range of 300 ℃ -500 ℃

                        · Has good adhesion

                        * Film with moisture, oil and atmospheric corrosion resistance performance

          Uses For the boiler, engine casing, exhaust pipes, chimneys, ovens and other high-temperature equipment, steel surface.

          Appearance of silver, film formation

          Construction parameters Volume solids of 39 ± 3% (according to GB / T9272 eqv ISO3233: 1998 Determination)

                            Dry film thickness of 20μm

                            The wet film thickness was 51 m

                            The theoretical amount of 55g / m2

          A flash point of 27 ° C

          Drying time (200 ± 2 ℃) ≤ 3h

          Overcoating interval The first paint film drying, until the cooling can be painted second paint.

          Recommended coating Road 1-2 Road, dry film thickness 20-40μm.

          Road before supporting paint

          · It can be directly applied to the surface of steel with Sa2.5 grade

          · E06-1 inorganic zinc silicate antirust paint can also be used as a primer to improve the anti-rust performance. General to E06-1 inorganic zinc silicate antirust paint a (40μm), 14 silver silicone high temperature baking 1-2 Road (20-40μm) is appropriate

          Surface treatment

          * There are oxide steel: sandblasting to Sa2.5 level

          * No oxide steel: Elastic grinding wheel grinding to St3 level

          · Steel with old paint: sandblasted to Sa2.5 grade; or after all the old paint films have been removed, grinding with elastic grinding wheel to St3 level

          · In order to get good use effect, after painting the first high temperature paint, should be heated to the working temperature, after cooling can be painted second

          Construction conditions

                        · Substrate temperature should be higher than 3 ℃ above the dew point, but not more than 60 ℃

                        · Relative humidity not more than 85%

          Coating method

          Airless spray

                    Diluent xylene

                    Dilution 0-5% (by weight of paint, but generally do not require dilution)

                    Nozzle diameter 0.4-0.5mm

                    The discharge pressure is 12 to 15 MPa (about 120 to 150 kg / cm2)

          Air spraying

                        Diluent xylene

                        Dilution 0-5% (by weight of paint, but generally do not require dilution)

                        Nozzle diameter of 2.0-3.0mm

                        Air pressure 0.3-0.5MPa (about 3-5kg / cm2)

          Roller coating / brushing generally do not require dilution

          Cleaning agent xylene

          Safety precautions Refer to the MSDS.

          Packaging 4L barrels 4kg

          Shelf life of 6 months.

          Remark For the correct use of our products, please carefully read the "User's Guide" in this manual.

          Statement The above data and data are based on our test and practical experience in the use of accumulated and can be used as construction guide. We do not understand the situation in the construction, we only guarantee the quality of the paint itself, other issues will not be responsible. For this manual, we will be based on the continuous improvement of products have the right to modify.

          If you have questions, you can:

          Or leave a message for us.

          Related recommendation
          Online Service




              <address id="9hx9l"></address>
              <form id="9hx9l"></form>
                <form id="9hx9l"></form>

                <form id="9hx9l"></form>