          85 silver high temperature paint

          Product introduction

          Form :
          Main characteristics :
          Purpose :
          Appearance :

          Composed of modified polyester, aluminum powder, heat-resistant pigments, additives and organic solvents such as the composition of high temperature paint.

          Key Features

                          Good heat resistance, can be used in the range of 200 -300

                         * Has the characteristics of self-drying at room temperature, and dry faster

                          Has good adhesion

                         * Film with moisture, oil, corrosion resistance to atmospheric corrosion of common media

          Uses For high-temperature boilers, chemical reactor kettle reactor and the need for high temperature, and can not bake the equipment and components.

          The appearance of silver-gray

          Construction parameters

          Volume of solid 38 3% (according to GB / T9272 eqvISO3233: 1998 provisions of the determination)

                         Dry film thickness of 20m

                         The wet film thickness was 53 m

                         Theoretical amount of 58g / m2

                         A flash point of 27 C

                         Drying time (25 )

          Surface dry 15min

                                      Hard work 24h

                                      Drying (150 2 ) 2h

          Overcoating interval time

          The temperature





          The shortest





          The longest


          Recommended coating number 2, dry film thickness 40m.

          Road before supporting paint

          It can be directly applied to the surface of steel with Sa2.5 grade

          E06-1 inorganic zinc silicate antirust paint can also be used as a primer to improve the anti-rust performance. General to E06-1 inorganic zinc silicate antirust paint 1 (40m), 85 silver high temperature paint 1-2 Road (20-40m) is appropriate

          Surface treatment

                         * There are oxide steel: sandblasting to Sa2.5 level

                         * No oxide steel: sandblasting to Sa2.5 level or to the abrasive wheel grinding to St3 level

                          Welding, flame cutting or fire work correction Burned parts: except for welding flux, welding slag, spatter after sandblasting to Sa2.5 level or with elastic grinding wheel to St3 level

                          Steel with old paint: sandblasted to Sa2.5 grade; or after all the old paint films have been removed, grinding with elastic grinding wheel to St3 level

                          In order to get good use effect, after painting the first high temperature paint, should be heated to the working temperature, after cooling can be painted second

          Construction conditions

                        Substrate temperature should be higher than 3 above the dew point, but not more than 60

                        Relative humidity not more than 85%

          Coating method

          Airless spray

                    Thinner xylene (under normal circumstances without diluent)

                    Dilution 0-5% (by weight of paint)

                    Nozzle diameter 0.4-0.5mm

                    The discharge pressure is 12 to 15 MPa (about 120 to 150 kg / cm2)

          Air spraying

                        Diluent xylene

                        Dilution 0-5% (by weight of paint)

                        Nozzle diameter of 2.0-3.0mm

                        Air pressure 0.3-0.5MPa (about 3-5kg / cm2)

          Roll coating / brushing

                        Diluent xylene

                        Dilution 0-3% (by weight of paint)

          Cleaning agent xylene

          Safety precautions Refer to the MSDS.


                        4L barrels 3.5kg

                        18.5L drums 17.5kg

          Shelf life of 6 months.

          Remark For the correct use of our products, please carefully read the "User's Guide" in this manual.

          Statement The above data and data are based on our test and practical experience in the use of accumulated and can be used as construction guide. We do not understand the situation in the construction, we only guarantee the quality of the paint itself, other issues will not be responsible. For this manual, we will be based on the continuous improvement of products have the right to modify.

          If you have questions, you can