          H06-2 water-based inorganic zinc-rich primer (two-component)

          Product introduction

          Form :
          Main characteristics :
          Purpose :
          Appearance :

          Product composition: The main components for containing water-based inorganic binder, silane coupling agent, zinc powder and special additives such as the composition of two-component anti-rust primer, with excellent corrosion resistance.

          Product performance: with the role of cathodic protection, anti-rust performance, in the sandblasting steel has excellent adhesion, excellent curing properties, excellent solvent resistance and temperature performance, fast drying.

          Usage: Mainly used for oil tank, marine steel structure, bridges, large steel structure and other metal surface corrosion protection.

          Construction parameters:

          Color: gray no light

          Specific gravity: about 2.8 kg / liter

          Dry film thickness: 50 microns

          Wet film thickness: 80 microns

          Theoretical consumption: 280 grams / square meter.

          Proportion: A component: B component = 7: 3 (weight ratio)

          Recommended Painting Road: airless spray together.

          Surface treatment: The surface to be coated must be sandblasted to St2.5.

          After the Road supporting coating: H06-4 epoxy cloud iron antirust paint.

          Substrate temperature: substrate temperature must be higher than the dew point above 3 ℃, outdoor temperature below 0 degrees, not suitable for outdoor construction.

          Construction Methods: Spraying (large caliber gun)

          Mixing: This product is divided into two cans, according to the proportion of a group of zinc powder into the B component, stirring evenly, while stirring side of the construction.

          Thinner: clean tap water.

          Dosage: 0-5% or as appropriate dilution.


          Zinc-rich zinc primer can form the surface of the primer in the paint after the paint should not be a long time before exposure. If you need a longer coating interval, it is recommended as soon as possible coating H06-4 epoxy cloud iron antirust paint for sealing.

          Packing: A component: 50kg B component: 21.5kg.

          Shelf Life: 6 months, subject to specified conditions.

          Note: For correct use of this product, please carefully read the instructions.

          Disclaimer: The above information and data is accumulated in the experimental conditions and actual use, and can be used as a construction guide. We only guarantee the quality of the paint, for this manual, we will be based on the continuous improvement of products are subject to change without notice.

          If you have questions, you can:

          Or leave a message for us.

          Related recommendation
          Online Service




              <address id="9hx9l"></address>
              <form id="9hx9l"></form>
                <form id="9hx9l"></form>

                <form id="9hx9l"></form>