By epoxy resin, red iron oxide and new rust-proof pigments, anti-rust additives, mixed solvents, polyamine compounds for the preparation of curing agent. A, B two-component packaging.
A room - temperature curing workshop anti - corrosion primer. Dry fast, excellent physical and mechanical properties of the coating, with various types of bottom, topcoat supporting the use of. Because it does not contain metal zinc and other substances, thereby reducing the welding gas on the human body harm.
Uses: Suitable for steel plate automatic shot blasting line and after rust as a primer. Dry film thickness to 25μm, the effective protection of the plate for about 6 months.
Theoretical dosage: 120-160g / ㎡
Wet film thickness: 80 μm
Dry film thickness: 20-25μm
Pot life: 23 ± 2 ℃ 8 hours
Drying time: dry 30 minutes, hard work 24 hours (23 ± 2 ℃, relative humidity 55 ± 5%), overcoating time: 23 ± 2 ℃ 24 hours
Recommended Painting Road: 1-2 Road.
After supporting the coating: epoxy resin coating, chlorosulfonated polyethylene paint, polyurethane coatings, chlorinated rubber coatings.
Surface treatment: to be painted surface must remove oil, water, rust and so on. There are oxide steel, sandblasting to St2.5.
No oxidation of steel, pneumatic, electric or hand-polished to St3 level.
Construction temperature: construction temperature below 5 ℃, should not be used.
Curing time: 23 ± 2 ℃ 30 minutes
Construction methods: spraying, brushing, roller coating
Thinner: XH-1 epoxy diluent
Dosage: 0-5% or as appropriate dilution.
Safety measures: pay attention to the construction site to have a good ventilation and other environmental protection measures, and is strictly prohibited fire.
Packing: Main paint: 24㎏ / barrel curing agent: 4kg / pot
Shelf life: 12 months under the conditions specified.
Note: For correct use of this product, please carefully read the instructions.
Disclaimer: The above information and data is accumulated in the experimental conditions and actual use, and can be used as a construction guide. We only guarantee the quality of the paint, for this manual, we will be based on the continuous improvement of products have the right to modify without notice
If you have questions, you can：
H06-11 steel structure epoxy zinc-rich primer (two-component)
H06-2 water-based inorganic zinc-rich primer (two-component)
H06-4 Antirust Paint for Epoxy Manganese Iron (Two-component)
H06-14 iron red / gray epoxy antirust primer (two-component)
H06-16 Gray zinc phosphate epoxy primer (two-component)