Products: from epoxy resin, anti-rust paint, all kinds of additives, curing agent composed of anti-rust paint.
Product performance: excellent resistance to salt water and anti-rust; anti-chemical and oil resistance; stability and adhesion.
Usage: The paint is suitable for steel structure, mine steel bracket, pipe and other anti-corrosion coatings.
Density: about 1.46 g / m2;
Theoretical dosage: 120-180g / m2
Dry film thickness: 45 μm
Drying time: surface dry ≤ 1h; hard work ≤ 24 h (23 ± 2 ℃, relative humidity 55 ± 5%)
Curing time: 15 minutes (23 ℃)
Applicable period: 6h (23 ℃)
Recommended coating number: 2, dry film thickness 60μm.
After supporting the road with paint: epoxy anticorrosive finish, acrylic paint, chlorinated rubber topcoat.
Surface treatment: a steel oxide: sandblasting to Sa2.5 level; zinc-plated substrate to remove the zinc salt after the construction;
Welding, flame cutting or fire work to correct the burning site to remove welding slag, splash, polished to St3 level; coated with workshop floor Paint the steel: the use of sandblasting or sandblasting to the elastic grinding wheel to St3 level.
Substrate temperature: substrate temperature should be higher than the dew point above 3 ℃
Construction methods: spraying, roller, brush
Thinner: XH-1 epoxy diluent
Airless Spray: Dilution: 5-10% (by weight of paint)
Nozzle diameter: 0.4-0.5 mm Spraying pressure: 20-30MPa
Air Spray: Dilution: 0-10% (by weight of paint)
Nozzle diameter: 2-3mm Spraying pressure: 0.2-0.4MPa
Roller / Brush: mainly used for small areas of painting and repair
Dilution: 0-5% (by weight of paint)
Safety measures: pay attention to the construction site to have a good ventilation and other environmental protection measures, and open flame is strictly prohibited.
Packing: Main paint: 24kg / barrel; curing agent: 4kg / pot.
Shelf life: 12 months in accordance with the provisions of the conditions.
Note: Please read the operating instructions carefully for the correct use of this product.
Disclaimer: The above information and data is accumulated in the experimental conditions and actual use, and can be used as a construction guide. We only guarantee the quality of the paint, for this manual, we will be based on the continuous improvement of products are subject to change without notice.
If you have questions, you can：
H06-11 steel structure epoxy zinc-rich primer (two-component)
H06-2 water-based inorganic zinc-rich primer (two-component)
H06-4 Antirust Paint for Epoxy Manganese Iron (Two-component)
H06-14 iron red / gray epoxy antirust primer (two-component)
H06-16 Gray zinc phosphate epoxy primer (two-component)