Product composition: Epoxy resin, scaly mica iron oxide, non-floating aluminum paste, anti-settling agent, anti-rust additives, solvents, curing agent made of. A, B two-component packaging.
Product performance: a higher shielding coating, containing a high pigment volume concentration of flake pigment, pigment composition after the film can be parallel to the orientation of overlapping arrangement, similar to "fish-like" lap structure, so there is a better Closed heat resistance and corrosion resistance.
Uses: It can be used as anti-corrosion coating primer, anti-corrosion coating can also be used as the middle of paint, and epoxy zinc-rich primer supporting the use of between the coating to enhance the sealing and anti-corrosion properties.
Theoretical dosage: 280g / ㎡
Wet film thickness: 200 μm Dry film thickness: 100 μm
Pot life: 23 ± 2 ℃ 8 hours
Drying time: dry 2 hours, hard work 24 hours (23 ± 2 ℃, relative humidity 55 ± 5%)
Overcoating time: 1-7 days at room temperature
Recommended Painting Road: No air spray 1, brush, roll 2
Former matching paint: H06-1 epoxy zinc-rich primer, inorganic zinc silicate primer.
After the Road supporting coatings: epoxy paint, epoxy asphalt coating, chlorinated rubber coatings, polyurethane coatings.
Surface treatment: Before the road paint should be completely dry. Surface to be painted must be cleaned of oil, water, dust and other debris.
Substrate temperature: the construction temperature is below 5 ℃, curing reaction is slow, should not be used.
Curing time: 23 ± 2 ℃ 30 minutes
Construction methods: spraying, roller coating.
Thinner: XH-1 epoxy diluent
Dosage: 0-5% or diluted as appropriate
Safety measures: pay attention to the construction site must have a good ventilation and other environmental protection measures, and is strictly prohibited fire.
Packing: Main paint: 24㎏ / barrel curing agent: 6kg / pot
Shelf Life: 12 months, subject to specified conditions
Note: For correct use of this product, please carefully read the instructions.
Disclaimer: The above information and data is accumulated in the experimental conditions and actual use, and can be used as a construction guide. We only guarantee the quality of the paint, for this manual, we will be based on the continuous improvement of products are subject to change without notice.
If you have questions, you can：
H06-11 steel structure epoxy zinc-rich primer (two-component)
H06-2 water-based inorganic zinc-rich primer (two-component)
H06-4 Antirust Paint for Epoxy Manganese Iron (Two-component)
H06-14 iron red / gray epoxy antirust primer (two-component)
H06-16 Gray zinc phosphate epoxy primer (two-component)