Composition: by the epoxy resin, phenolic coal tar pitch, rust paint, thickener and curing agent composed of two-component coating.
Performance: Tough film adhesion, and has excellent corrosion resistance. Long-term protection in the marine and other harsh environments.
Uses: The paint is widely used in buried pipes, steel, wood products, cement products such as surface corrosion and general atmospheric corrosion coating.
Specific gravity: about 1.20 g / m3
Theoretical dosage: 270g / m2
Wet film thickness: 225 μm
Dry film thickness: 125 μm
Flash point: 28 ℃
Drying time: dry 6 hours, hard work 24 hours (23 ± 2 ℃)
Maturation time: at room temperature: 0.5 hours
Painting interval: 24 hours
Construction Reference: Recommended Painting Road: 2
Former matching paint: H06-1 epoxy zinc-rich primer, H06-14 epoxy iron oxide red primer, inorganic zinc silicate primer.
Surface treatment: If coated directly on steel, steel shot blasting or sandblasting to be handled to achieve the Swedish derusting standard Sa2.5 level;
In the workshop with a primer on the surface will be subject to secondary derusting, to the Swedish derusting St3 standard.
Substrate temperature: substrate temperature should be higher than the dew point above 3 ℃, relative humidity should be less than 85%.
Construction methods: spraying, brushing, roller coating
Thinner: XH-1 epoxy diluent
Dosage: 0-10% (by weight)
Avoid long-term inhalation of solvent vapors or mist, skin, eyes can not contact the goods, in the narrow or air is not circulation construction, must provide strong ventilation, construction should wear protective equipment.
Packing: Main paint: 20kg / barrel curing agent: 5kg / barrel
Shelf life: 12 months under the specified conditions.
Note: For correct use of this product, please carefully read the instructions.
Disclaimer: The above information and data is accumulated in the experimental conditions and actual use, and can be used as a construction guide. We only guarantee the quality of the paint, for this manual, we will be based on the continuous improvement of products are subject to change without notice.
If you have questions, you can：
H06-11 steel structure epoxy zinc-rich primer (two-component)
H06-2 water-based inorganic zinc-rich primer (two-component)
H06-4 Antirust Paint for Epoxy Manganese Iron (Two-component)
H06-14 iron red / gray epoxy antirust primer (two-component)
H06-16 Gray zinc phosphate epoxy primer (two-component)