Composition: from the hydroxyl-containing resin, curing agent, pigments, additives and solvents from the preparation.

Performance: good wear resistance coating, tough plump, bright color, oil, water, has good corrosion resistance.

Uses: Apply to the surface of steel for anti-corrosion finish, but also for wood and cement products, marine machine tools, electrical appliances, such as surface protection and decorative finish.

Construction parameters:

Theoretical dosage: 140-160 g / ㎡ printing, brushing 90-100 g / ㎡

Wet film thickness: 80 μm. Dry film thickness: 30-35μm

Pot life: 23 ℃ 8 hours

Drying time: 23 ± 2 ℃, surface dry 2 hours, hard work 24 hours, fully cured for 7 days.

Maturation time: 20 minutes

Overcoating time:

Construction Reference:

Recommended coating number: 2.

After supporting the coating: epoxy iron red primer, polyurethane red iron paint.

Surface treatment: If the oil surface to be painted must be cleaned, and dry. If primer primer, it should be dry after the primer with polished smooth sandpaper and then applied.

Substrate temperature: Substrate temperature must be higher than the dew point above 3 ℃, relative humidity should be less than 75%.

Construction methods: brushing, spraying

Thinner: XZ-1 polyurethane thinner

Dosage: 0-10% by weight or, as appropriate, diluted.

Safety measures: in the narrow or limited space construction, ventilation must be strengthened and open flame is strictly prohibited

Packing: Main paint: 21kg / barrel, curing agent: 7kg / pot.

Shelf Life: 12 months, subject to specified conditions

Note: For correct use of this product, please carefully read the instructions.

Disclaimer: The above information and data is accumulated in the experimental conditions and actual use, and can be used as a construction guide. We only guarantee the quality of the paint, for this manual, we will be based on the continuous improvement of products are subject to change without notice.